GRC轻质构件开裂有哪些解决途径?
来源: 关键词:GRC构件 发布时间:2018-07-24 阅读:214

                                       

GRC轻质构件开裂通过改善构件材性的解决途径
Solution to cracking of GRC lightweight components by improving material properties of components
改善构件的材性主要应达到两个目标:一是降低构件的收缩值,其中包含干缩值和冷缩值,以减少构件的收缩变形;二是提高构件和接缝材料的弹性,增加拉伸变形值。通过这“一增一减”来尽量达到构件的收缩变形与拉伸变形的平衡。但目前GRC轻质构件的特性使拉伸值与收缩值平衡比较有困难。
Two objectives should be achieved to improve the material properties of the components: one is to reduce the shrinkage value of the components, including shrinkage and cold shrinkage values, in order to reduce the shrinkage deion of the components; the two is to improve the elasticity of the components and joint materials and increase the tensile deion value. The balance between shrinkage deion and tensile deion can be achieved by "one increase, one decrease" as far as possible. However, the current characteristics of GRC lightweight components make it difficult to balance the tensile and shrinkage values.

 
 

分享到:
打印本页 || 关闭窗口
新闻中心
联系我们 更多

广航新型建筑材料有限公司

  • 地 址:杭州市余杭区五常荆山湾路88号
  • 邮 编:310024
  • 联 系 人:潘光(经理)
  • 手 机:15088583535 13575792211
  • 电子邮箱:guanghangjc@163.com
广航新型建筑材料有限公司 2012-2015 天天彩票xgtty.com版权所有 Copyright 2012 Auto Parts All Right Reserved 备案号:浙ICP备12021499号
首页| 网站首页| 关于我们| 新闻中心| 产品中心| 业务范围| 人才招聘| 下载中心| 在线留言| 联系我们|网站地图
友情链接:天天彩票  天天彩票官方手机版  天天彩票网投注  天天彩票开户  天天彩票官网  天天彩票计划网  天天彩票网址  天天彩票网投注  

免责声明: 本站资料及图片来源互联网文章,本网不承担任何由内容信息所引起的争议和法律责任。所有作品版权归原创作者所有,与本站立场无关,如用户分享不慎侵犯了您的权益,请联系我们告知,我们将做删除处理!